310S Plata steela sterilis
310SStella austenitica est,It combines excellent high-temperature performance with good ductility and weldability。Usum est ad aplicationes altas temperaturae,Pro altum chromium et nitrum2100°FProvides solid corrosion resistance at high temperature、Excellent antioxidant properties and outstanding strength。Pro altum chromium et nitrum,Melior quam in multis environamentibus304forsit309Stella inmaculata。
product description
310SStella austenitica est,It combines excellent high-temperature performance with good ductility and weldability。Usum est ad aplicationes altas temperaturae,Pro altum chromium et nitrum2100°FProvides solid corrosion resistance at high temperature、Excellent antioxidant properties and outstanding strength。Pro altum chromium et nitrum,Melior quam in multis environamentibus304forsit309Stella inmaculata。
Parametri produktorum
Product name | 310S Plata steela sterilis |
type | tabula |
densitatem | 0.3-200mm |
longitudo | 2000mm / 2438mm / 3000mm / 5800mm / 6000mm / 12000mmclassClass |
latitudinem | 40mm-600mm / 1000mm / 1219mm / 1500mm / 1800mm / 2000mm / 2500mm / 3000mm / 3500mmclassClass |
standard | ASTM / AISI / JIS / GB / DIN / EN |
superficie | BA / 2B / NO.1 / NO.4 / 4K / HL / 8KclassClass |
Programma | Widely used in high temperature and electrical industry、Equatoria medica aedificata、chemia、alimenta industria、Agricultural and ship components、Cibus et biberibus packaging、 Kitina provisiones、tren、aeroplane、cinerem conveyer、vehiculum、bolt、nut、Springs and mesh screens, etc. |
certificatus | ISO / SGS / BV |
production technology | hot-rolling / frigidus volans |
print operation status | print operation status / Trying to try |
composition chemical
C | Si | Mn | Cr | Ni | S | P |
≤0.08 | ≤1.0 | ≤2.0 | 24.0~26.0 | 19.0~22.0 | ≤0.03 | ≤0.045 |
Proprietates mechanicae
tensile strength σb (MPa) | yield strength σ0.2 (MPa) | elongation δ5 (%) | duritia |
≥520 | ≥205 | ≥40 | ≤217HB;≤95HRB |
proprietatem physicam
densitate(g/cm³) | Elastic modulus(Gpa) | Thermal expansion coefficient(10-6/ºC) | conductivitate thermal(W/m*K) | resistentia(µΩ.cm) |
9.01 | 200 | 14.4 | 13.8 | 94 |
Selection superficie